Abstract We assessed the effect of a new coating material based on resin-modified glass-ionomer with calcium (Ca) in inhibiting the demineralization of underlying and adjacent areas surrounding caries-like lesions in enamel. The measures used were surface hardness (SH) and cross-sectional hardness (CSH). Thirty-six bovine enamel specimens (3 × 6 × 2 mm) were randomly allocated into three groups (n = 12): No treatment (NT); resin-modified glass-ionomer with Ca (Clinpro XT Varnish, 3M ESPE) (CL), and fluoride varnish (Duraphat, Colgate) (DU). The specimens were subjected to alternated immersions in demineralizing (6 h) and remineralizing solutions (18 h) for 7 days. SH measurements were conducted at standard distances of 150, 300, and 450 µm from the treatment area. CSH evaluated the mean hardness profile over the depth of the enamel surface and at standard distances from the materials. The energy-dispersive X-ray spectroscopy analysis was conducted to evaluate the demineralization bands created on the sublayer by % of calcium (Ca), phosphorus (P), and fluoride (F). Ca/P weight ratio was also calculated. Based on SH and CSH measurements, there was no difference between groups at the distances 150 µm (p = 0.882), 300 µm (p = 0.995), and 450 µm (p = 0.998). Up to 50 µm depth (at 150 µm from the treatment area), CL showed better performance than DU ( p< 0.05). NT presented higher loss of Ca and P than CL and DU (p < 0.05). There was no significant difference in the % of F ion among the three groups. The new coating material was similar to F varnish in attenuating enamel demineralization.

Abstract Objective This study aimed to analyze the following physicochemical properties: radiopacity, final setting time, calcium release, pH change, solubility, water sorption, porosity, surface morphology, and apatite-forming ability of two calcium silicate-based materials. Material and methods We tested MTA Repair HP and MTA Vitalcem in comparison with conventional MTA, analyzing radiopacity and final setting time. Water absorption, interconnected pores and apparent porosity were measured after 24-h immersion in deionized water at 37°C. Calcium and pH were tested up to 28 d in deionized water. We analyzed data using two-way ANOVA with Student-Newman-Keuls tests (p<0.05). We performed morphological and chemical analyses of the material surfaces using ESEM/EDX after 28 d in HBSS. Results MTA Repair HP showed similar radiopacity to that of conventional MTA. All materials showed a marked alkalinizing activity within 3 h, which continued for 28 d. MTA Repair HP showed the highest calcium release at 28 d (p<0.05). MTA Vitalcem showed statistically higher water sorption and solubility values (p<0.05). All materials showed the ability to nucleate calcium phosphate on their surface after 28 d in HBSS. Conclusions MTA Repair HP and MTA Vitalcem had extended alkalinizing activity and calcium release that favored calcium phosphate nucleation. The presence of the plasticizer in MTA HP might increase its solubility and porosity. The radiopacifier calcium tungstate can be used to replace bismuth oxide.

Abstract: The aim of this study was to compare the efficacy of passive ultrasonic irrigation and EasyClean for removing residual filling material in retreatment. Twenty-two maxillary lateral incisors with apical curvature were instrumented with ProTaper files and filled with Endofill using the lateral compactation technique. Removal of filling material was performed with Reciproc, Mtwo and ProDesign Logic 50/.01 files. The teeth were inserted in a silicone mould, which was placed in a metal muffle, and split to visualize the residual filling material. The samples were divided into two groups (n = 11) according to the irrigation protocol: Passive ultrasonic irrigation (PUI group) with 3 activations of 20 seconds and EasyClean (Easy Equipamentos Odontológicos, Belo Horizonte, Brazil) (EC group) used in continuous rotation with 3 activations of 20 seconds, both using NaOCl and EDTA. Environmental scanning electron microscopic images of the apical, middle, and cervical thirds were taken before and after the irrigant activation. The Kappa test was used to determine interexaminer agreement. Statistical analysis was performed using Kruskal–Wallis, Mann–Whitney, and Wilcoxon tests (p < 0.05). PUI and EC improved the removal of remnant filling material in all root canal thirds (p < 0.05). PUI and EC presented similar performance in the final step of retreatment (p > 0.05). No significant difference was observed in the removal of filling material in the apical, middle, and cervical thirds in both groups (p > 0.05). EasyClean in continuous rotary motion is useful in retreatment and was shown to be as effective as ultrasonic activation in the removal of remnant filling material.

RESUMO Objetivo: Avaliar a influência do preparo cervical utilizando a broca LA-Axxess nº 1 (SybronEndo, Glendora, EUA) ou os instrumentos ProTaper S1 e SX (Dentsply Maillefer, Ballaigues, Suíça) na precisão dos Localizadores Apicais Eletrônicos (LAEs): Root ZX mini (J. Morita Corporation, Tóquio, Japão) e Joypex 5 (Denjoy, Changsha, China). Métodos: Trinta incisivos inferiores foram acessados e o comprimento do canal radicular (CCR) determinado com uma lima K #15 com o auxílio de um estereomicroscópio. Em seguida, os dentes foram distribuídos em dois grupos (n=15) referentes ao preparo cervical com LA-Axxess ou instrumentos ProTaper. Os dentes foram incluídos em alginato e o CCR determinado pelos LAEs antes e após o preparo cervical. Os dados foram classificados em: precisos, se a diferença na medida do CCR era ≤ 0,05 mm; e imprecisos, se a diferença era >0,5 mm ou estava além do CCR. Resultados: O teste de McNemar (α<0.05) foi utilizado para detectar diferenças na precisão dos LAEs antes e após o preparo com os diversos instrumentos, e para detectar diferenças na precisão entre os aparelhos. Não foram identificadas diferenças na precisão entre os dois LAEs (P>0,05) após o preparo cervical, indiferente do instrumento utilizado. Conclusão: O preparo cervical aumentou o número de medições precisas dos LAEs, com diferença estatística para Joypex 5 após o uso da LA-Axxess, contudo os aparelhos apresentaram precisão similar após o preparo cervical, indiferente do instrumento utilizado.

ABSTRACT Objective: This study was aimed at evaluating the influence of cervical preflaring using LA-Axxes No. 1 bur (SybronEndo, Glendora, USA) or S1 and SX ProTaper files (Dentsply Maillefer, Ballaigues, Switzerland) on the accuracy of the Electronic Apex Locators (EALs): Root ZX mini (J. Morita Corporation, Tokyo, Japan), and Joypex 5 (Denjoy, Changsha, China). Methods: Thirty mandibular incisors were accessed, and the root canal length (RCL) was determined with a K-file #15, with the aid of a stereo microscope. Afterwards, the specimens were divided into 2 groups (n = 15) referring to the cervical preflaring with LA-Axxess or ProTaper files. The teeth were embedded in alginate and the RCL was determined by the EALs before and after preflaring. Data were classified into: accurate, if the difference in RCL measurement were ≤0.05 mm; and inaccurate, if the difference were >0.5 mm or beyond the RCL. Results: McNemar's test (α<0.05) was used to detect differences in the accuracy of the EALs before and after each preflaring with different instruments, and to detect difference in accuracy among devices. No differences were found concerning the accuracy of the EALs (P > 0.05) after the cervical preflaring, regardless of the used instrument. Conclusion: The preflaring procedure increased the number of accurate measurements for both EALs, with statistical difference for Joypex 5 when the preflaring was performed with LA-Axxess. However, after the cervical preflaring, the EALs showed similar accuracy, regardless of the used instrument.

Objectives: To investigate if there is a relation between the increase of bismuth oxide and the decrease of pH levels and an intensification of toxicity in the Portland cement. Material and Methods: White Portland cement (WPC) was mixed with 0, 15, 20, 30 and 50% bismuth oxide, in weight. For the pH level test, polyethylene tubes were filled with the cements and immersed in Milli-Q water for 15, 30 and 60 days. After each period, the increase of the pH level was assessed. For the biocompatibility, two polyethylene tubes filled with the cements were implanted in ninety albino rats (n=6). The analysis of the intensity of the inflammatory infiltrate was performed after 15, 30 and 60 days. The statistical analysis was performed using the Kruskal-Wallis, Dunn and Friedman tests for the pH level and the Kruskal-Wallis and Dunn tests for the biological analysis (p<0.05). Results: The results showed an increase of the pH level after 15 days, followed by a slight increase after 30 days and a decrease after 60 days. There were no significant statistical differences among the groups (p>0.05). For the inflammatory infiltrates, no significant statistical differences were found among the groups in each period (p>0.05). The 15% WPC showed a significant decrease of the inflammatory infiltrate from 15 to 30 and 60 days (p<0.05). Conclusions: The addition of bismuth oxide into Portland cement did not affect the pH level and the biological response. The concentration of 15% of bismuth oxide resulted in significant reduction in inflammatory response in comparison with the other concentrations evaluated.

O presente estudo avaliou, in vitro, o efeito antimicrobiano das proteínas salivares lactoferrina e lisozima sobre micro-organismos envolvidos no processo carioso, obtendo suas concentrações inibitórias mínimas (CIM) e bactericidas mínimas (CBM). Cepas de Streptococcus mutans (ATCC 25175) e Lactobacillus casei (ATCC 7469) foram submetidas a macrodiluição em caldo das soluções de lisozima a 80 mg/mL e lactoferrina a 200 mg/mL. A leitura dos tubos foi realizada em espectrofotômetro, após a incubação a 37 °C por 18 h em estufa de CO2, para verificação da CIM. Uma nova subcultura foi semeada em placas de ágar para a obtenção da CBM. O método de difusão em ágar foi também testado utilizando-se placas de Petri com ágar BHI com 100 µL do inóculo microbiano padronizado. Discos de filtro de papel embebidos com 10 µL das soluções de lactoferrina (200 µg/mL) e lisozima (80 µg/mL) foram colocados sobre a superfície do ágar. Não foi observado halo de inibição nas placas, demonstrando ausência de efeito antimicrobiano das proteínas neste teste. Os efeitos bactericida e bacteriostático da lisozima sobre L. casei foram 50,3 mg/mL e 43,1 mg/mL respectivamente. Os efeitos bactericida e bacteriostático sobre S. mutans foram 68,5 mg/mL e 58,7 mg/mL. A lactoferrina não induziu nenhum efeito inibitório sobre nenhuma bactéria, mesmo na concentração de 200 mg/mL. Não houve efeito antimicrobiano sinérgico das proteínas, quando testadas conjuntamente, e mesmo até em concentrações de 42,8 mg/mL de lisozima e 114 mg/mL de lactoferrina (os maiores valores avaliados). S. mutans e L. casei foram inibidos somente pela lisozima, não sendo afetados pela lactoferrina e pelo uso sinérgico de ambas proteínas.

The present study evaluated the antimicrobial in vitro effects of the salivary proteins lactoferrin and lysozyme on microorganisms involved in the carious process, obtaining their minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC). Streptococcus mutans (ATCC 25175) and Lactobacillus casei (ATCC 7469) were submitted to broth macrodilution of lysozyme at 80 mg/mL and lactoferrin at 200 mg/mL. The tubes were read in a spectrophotometer after they had been incubated at 37 °C for 18 h, in a carbon dioxide chamber, in order to read the MIC. A new subculture was carried on agar plates to obtain the MBC. The agar diffusion method was also tested, using BHI agar with 100 µL of the standardized microbial inocula. Filter-paper disks soaked in 10 µL of the solutions lactoferrin (200 µg/mL) and lysozyme (80 µg/mL) were placed on the agar surface. Inhibition halos were not observed on the plates, showing the absence of the antimicrobial effects of these proteins in this method. The bactericidal and bacteriostatic effects of lysozyme on L. casei were 50.3 mg/mL and 43.1 mg/mL respectively. The bactericidal and bacteriostatic effects on S. mutans were 68.5 mg/mL and 58.7 mg/mL. Lactoferrin did not induce any inhibitory effects on any microorganism, even in the concentration of 200 mg/mL. There was not a synergic antimicrobial effect of proteins, when they were tested together, even in the concentration of 42.8 mg/mL of lysozyme and 114 mg/mL of lactoferrin (the highest values evaluated). S. mutans and L. casei were only inhibited by lysozyme, not affected by lactoferrin and by the synergic use of both proteins.

This study compared the fluid filtration, adaptation to the root canal walls, and the push-out bond strength of two resin-based sealers and three calcium silicate-based retrograde filling materials. Fifty maxillary canines were shaped using manual instruments and the apical portion was sectioned. Retrograde cavities of 3-mm depth were prepared. The specimens were divided into five groups (n = 10): Sealer 26 (S26); MBPc (experimental); MTA; Portland cement with 20% zirconium oxide (PC/ZO), and Portland cement with 20% calcium tungstate (PC/CT). The fluid filtration was measured at 7 and 15 days. To evaluate the interfacial adaptation, sections of the teeth, 1 and 2 mm from the apex, were prepared and the percentage of gaps was calculated. The push-out bond strength at 2 mm from the apex was evaluated. Statistical analysis was performed using the ANOVA/Tukey’s test (p < 0.05). At 7 and 15 days (p = 0.0048, p = 0.006), the PC/CT group showed higher fluid filtration values when compared to other groups. At 1 mm from the apex, no statistical differences in the adaptation were found among the cements (p = 0.44). At 2 mm from the apex, the PC/ZO group presented statistically lower percentage of gaps than S26, MBPc, and MTA (p = 0.0007). The MBPc group showed higher push-out bond strength than other cements evaluated (p = 0.0008). The fluid filtration and interfacial adaptation of the calcium silicate-based cements were similar to those of the resin-based cements. The resinous cement MBPc showed superior push-out bond strength.